I’m trying to diagnose what tuning I need to get a smooth top layer on a solid print.

The picture you see is a 50mmx50mmx1mm square (cube([50,50,1]); in openscad) printed with a .4 nozzle. (5 layers)

For tuning on the problem, I have looked into:

  • z_offset – tried all kinds of values and if I reduce it anymore, it doesn’t squish into the bed and the center part is exactly 1mm – so unlikely to be that.
  • bed level – bltouch is working well
  • extrusion (esteps or rotational_distance) - played with this a great deal and any less and i start to have under-extrusion in the center area.
  • different filament – same with PLA, PETG and ABS
  • Different slicer – same with PrusaSlicer or Cura
  • Different speeds – one on the left was printed at 20mm/s – the right was printed at 150mm/s

I also cant find any guides out there that show this issue. Anybody with some suggestions or threads I can pull?

  • LazaroFlim@lemmy.film
    link
    fedilink
    English
    arrow-up
    7
    ·
    1 year ago

    Pressure advance will solve some of your issues here. When reaching a corner, the head slows down but the filament is still pushed too fast and so it overflows. Pressure advance (in Klipper) can compensate for that.

    • tenzen@lemmy.caOP
      link
      fedilink
      English
      arrow-up
      2
      ·
      edit-2
      1 year ago

      I’ll check that out. I installed klipper yesterday for S&G – actually quite liking the flexibility it gives me. I see the guide.

      • LazaroFlim@lemmy.film
        link
        fedilink
        English
        arrow-up
        4
        ·
        1 year ago

        Welcome to the deepest rabbit hole in 3D printing! Klipper is nice on the surface and absolutely mind blowing when you dig deeper. If you’re programming savvy, you can make it do basically anything. You can even install a script that runs shell scripts on the pi from the printer. You could make it control your coffee maker via home automation if you wanted. Lol. Anyways. Pressure advance is the key here.

        • tenzen@lemmy.caOP
          link
          fedilink
          English
          arrow-up
          4
          ·
          1 year ago

          Oh boy… Yes scripting comes easy to me. It’s why my default is openscad for making 3d models. :). I’m printing the pressure advance cube model now.

          • tenzen@lemmy.caOP
            link
            fedilink
            English
            arrow-up
            2
            ·
            1 year ago

            So… I still have some tuning.

            I learned that you need to adjust retraction and z offset again after implementing pressure advance… But I’m close now.

  • de_ninja@lemmy.world
    link
    fedilink
    English
    arrow-up
    5
    ·
    1 year ago

    Seems like it’s squishing when the printhead decelerates and accelerates again around the corner. Perhaps the temperature is too high so too much material oozes out when speed is decreases?

    • tenzen@lemmy.caOP
      link
      fedilink
      English
      arrow-up
      2
      ·
      edit-2
      1 year ago

      I agree, not just the perimeter but also when it’s going back and forth to fill in the centre area. I’m not sure how to address it – maybe the pressure advance settings LazaroFilm suggested. I’ve also tried printing at a series of different temperatures…

      • de_ninja@lemmy.world
        link
        fedilink
        English
        arrow-up
        1
        ·
        1 year ago

        That’s what I meant, have you tried just decreasing the printing temp by 10 degrees and then printing another square and comparing the result?

  • rambos@lemmy.world
    link
    fedilink
    English
    arrow-up
    4
    ·
    1 year ago

    It looks like overextrusion, but Im not sure. Did you change overlap settings?

    I would try with taller cube to eliminate 1st layer error. You might be overextruding, but due to higher nozzle distance your first layer can still look perfect

    • tenzen@lemmy.caOP
      link
      fedilink
      English
      arrow-up
      1
      ·
      1 year ago

      No, overlap settings are default. Taller objects or objects with infill come out okay - workable but still show small signs of the issue. I’ve found the 5+ layer object with no infill showes the issue the most so I’ve been using that to tune.

      You are absolutely correct that first layer tends not now show issues like zOffset to close to bed or over extrusion. The prints I’ve been using are 5+ solid layers to have any offset alignment or extrusion alignment issues increase with each added layer.

  • Guy_Fieris_Hair@lemmy.world
    link
    fedilink
    English
    arrow-up
    2
    ·
    edit-2
    1 year ago

    Looks like the edges are lifting from the bed a bit? What is the bed temp? Also, maybe lower the z offset? Doesn’t seem to be geting enough squish maybe. Hard to tell from the pictures.

    • tenzen@lemmy.caOP
      link
      fedilink
      English
      arrow-up
      1
      ·
      1 year ago

      in those two cases, they are PETG and bed temp was 80. The curved edges were caused by me removing the print from the hot bed… not lifting off during the print.

  • tenzen@lemmy.caOP
    link
    fedilink
    English
    arrow-up
    1
    ·
    1 year ago

    Thank you everybody for leading me on the right path.

    As I had already installed Klipper, I decided to try the pressure advance calibration as suggested and it did take some tuning, but has improved quality immensely.

    In the end, here are the settings I changed: Klipper printer.cfg pressure_advance: 0.120

    PrusaSlicer:PrinterSettings:Extruder 1:Retraction Length: 0

    I still think I can tweak my z-offset and temperature and maybe further refine pressure_advance, but the results are quite a bit better than before.

    I used the Klipper guide for pressure advance: https://www.klipper3d.org/Pressure_Advance.html

    Original print on the left, print with the above changes on the right.

    Having said that, I think I might have been able to improve the results using a marlin firmware and working with my retraction setup – I use a non-default direct-drive extruder so the default settings of about 6mm are certainly incorrect.

    Also, into the future, i’ll check out the wear/maintenance on the nozzle – it is a good point and I havent changed it in quite a few prints.

    Thank you everybody!